Rigid Polyurethane Pen Tane Blown System Formulated Blend Polyol for Dis-Continous Sandwich Panel

Model NO.
LY-6134
Shelf Life
6 Months
Free Rise Density
32-35 Kg/M3
Density at 25°c
Approx. 1.16
Ratio Polyol: Isocyanate
100:100
Viscosity at 25°c
Approx. 625
Transport Package
Steel Drum/IBC Drum/Tank
Specification
pure
Trademark
G-TECH@
Origin
China
HS Code
390931
Production Capacity
30000mt/Year
Package Size
60.00cm * 60.00cm * 102.00cm
Package Gross Weight
218.000kg
Reference Price
$ 2.70 - 16.20
Contact Us

Product Description

BLEND POLYOL  LY-6134
 
Application LY-6134  is a formulated polyol developed for the production of discontinuous panels according to B2-DIN 4102.
This polyol is a mixture of polyetherpolyols, glycols, actibators (contains amine), flame retardent and stabilizer.
It is based on Diphenylmethandiisocyanate (MDI).
Specification and typical properties   Polyol  Isocyanate
Viscosity at 25°C Approx. 625 Approx. 200 mPa.s
Density at 25°C Approx. 1.16 Approx. 1.23 g/cm 3
Processing conditions and performance LY-6134 /
HCFC 141B /
ISO 6134 /
Ratio Polyol: Isocyanate 100:100
Material temperature 20°C
Moulds temperature / °C
Demoulding time depending on thicknesses /  minutes
CUP test -Material temperature 20°C
-Cup weight -Polyol /  g
-Isocyanate /  g
-Parameter -Cream time /  sec.
-Gel time /  sec.
-Free rise density 32-35 kg/m 3
Shelf life is guaranteed for 6  months.

Rigid Polyurethane Pen Tane Blown System Formulated Blend Polyol for Dis-Continous Sandwich Panel Rigid Polyurethane Pen Tane Blown System Formulated Blend Polyol for Dis-Continous Sandwich Panel Rigid Polyurethane Pen Tane Blown System Formulated Blend Polyol for Dis-Continous Sandwich Panel Rigid Polyurethane Pen Tane Blown System Formulated Blend Polyol for Dis-Continous Sandwich Panel

 

Polymer & Resin