| HRC50 | HRC55 | HRC60 | HRC65 |
| YG10X | YG10.2 &WF25 (Taiwán) | K44 y K40 | Sandvik H10F |
|
Talla de grano: 0.7um
Co: 10 % Fuerza flexural: 3320N/mm2 |
Talla de grano: 0.6um
Co: 10 % Fuerza flexural: 4000N/mm2 |
Talla de grano: 0.5um
Co: 12 % Fuerza flexural: 4300N/mm2 |
Talla de grano: 0.4um
Co: 12.5 % Fuerza flexural: 4300N/mm2 |
|
|
AlTiN | TiAIN | TiSiN | Nano |
| Dureza (alto voltaje) | 3200 | 2800 | 3600 | 42 (GPA) |
| Espesor (UM) | 2.5-3 | 2.5-3 | 3 | 3 |
| Temp de la oxidación (°) | 900 | 800 | 1000 | 1200 |
| Fricción Coeffient | 0.3 | 0.3 | 0.45 | 0.4 |
| Color | Negro | Violeta | Cobre | Azul |
| 1.0× 3× 4D× 50L× 4F | 1 | 3 | 4 | 50 |
| 1.5× 4× 4D× 50L× 4F | 1.5 | 4 | 4 | 50 |
| 2.0× 6× 4D× 50L× 4F | 2 | 6 | 4 | 50 |
| 2.5× 8× 4D× 50L× 4F | 2.5 | 8 | 4 | 50 |
| 3.0× 8× 4D× 50L× 4F | 3 | 8 | 6 | 50 |
| 3.5× 10× 4D× 50L× 4F | 3.5 | 10 | 6 | 50 |
| 4.0× 11× 4D× 50L× 4F | 4 | 11 | 6 | 50 |
| 4.5× 13× 6D× 50L× 4F | 4.5 | 13 | 6 | 50 |
| 5.0× 13× 6D× 50L× 4F | 5 | 13 | 6 | 50 |
| 5.5× 13× 6D× 50L× 4F | 5.5 | 13 | 6 | 50 |
| 6.0× 15× 6D× 50L× 4F | 6 | 15 | 6 | 50 |
| 7.0× 16× 8D× 60L× 4F | 7 | 16 | 8 | 60 |
| 8.0× 20× 8D× 60L× 4F | 8 | 20 | 8 | 60 |
| 9.0× 20× 10D× 75L× 4F | 9 | 20 | 10 | 75 |
| 10× 25× 10D× 75L× 4F | 10 | 25 | 10 | 75 |
| 11× 25× 12D× 75L× 4F | 11 | 25 | 12 | 75 |
| 12× 30× 12D× 75L× 4F | 12 | 30 | 12 | 75 |
| 14× 35× 14D× 100L× 4F | 14 | 35 | 14 | 100 |
| 16× 40× 16D× 100L× 4F | 16 | 40 | 16 | 100 |
| 18× 45× 18D× 100L× 4F | 18 | 45 | 18 | 100 |
| 20× 45× 20D× 100L× 4F | 20 | 45 | 20 | 100 |