Fabric
type |
Fabric structure |
Fabric
Specs |
Ply thick
(mm/p) |
Strength Series (N/mm) | Cover thickness (mm) |
Width
(mm) |
Length
(mm) |
||||||
Warp | Weft | 2ply | 3ply | 4ply | 5ply | 6ply | Upper | Lower | |||||
EP
(Poly Ester) |
E
(Polyester) |
P
(Ny lon) |
EP80 | 0.60 | 160 | 240 | 320 | 400 | 480 | 2.0-8 | 0-4.5 |
400-
2200 |
≤250 |
EP100 | 0.75 | 200 | 300 | 400 | 500 | 600 | |||||||
EP150 | 1.00 | 300 | 450 | 600 | 750 | 900 |
500-
2200 |
||||||
EP200 | 1.10 | 400 | 600 | 800 | 1000 | 1200 | |||||||
EP250 | 1.25 | 500 | 750 | 1000 | 1250 | 1500 | |||||||
EP300 | 1.35 | 600 | 900 | 1200 | 1500 | 1800 | |||||||
EP350 | 1.45 | 1050 | 1400 | 1750 | 2100 | 800-2200 | |||||||
EP400 | 1.55 | 1600 | 2000 | 2400 | 1000-2200 | ||||||||
EP500 | 1.70 | 2000 | 2500 | 3000 |
Standard | Rubber Cover | Adhension | ||||
Tension | Elongation | Abrasive | C to ply | C to ply | Ply to Ply | |
DIN22102 | Mpa | % | Mm3 | N/mm ≤ | N/mm > | N/mm |
Z | 15 | 350 | 250 | 3.5 | 4.5 | 5 |
W | 18 | 400 | 90 | 3.5 | 4.5 | 5 |
Y | 20 | 400 | 150 | 3.5 | 4.5 | 5 |
X | 25 | 450 | 120 | 3.5 | 4.5 | 5 |
Standard | Rubber Cover | Adhension | ||||
Tension | Elongation | Abrasive | C to ply | C to ply | Ply to Ply | |
RMA | Mpa | % | Mm3 |
N/mm
≤ |
N/mm
> |
N/mm |
RMA-I | 14 | 350 | 250 | 3.5 | 4.5 | 5 |
RMA-II | 17 | 400 | 175 | 3.5 | 4.5 | 5 |
Standard | Tension | Abrasion | Elongation | Adhesion |
AS 1332-2000 | Mpa | mm 3 | % | N/mm |
A | 17 | 70 | 400 | 6 |
E | 14 | -- | 300 | 6 |
F | 14 | -- | 300 | 6 |
M | 24 | 125 | 450 | 6 |
N | 17 | 200 | 400 | 6 |
S | 14 | 250 | 300 | 6 |