| Test Method | Test Item | Result | |
| ISO 4892-2 | Xenon Arc Weathering | Non-exposure | 2000h Exposure |
| ISO 4892-2 | Color Change | - | Gray Scale 3 |
| ISO 178 |
Flexural Strength
Flexural Modulus |
26.3Mpa
2.4Gpa |
25.0 Mpa, decrease 4.9%
2.24GPa,decrease 8.2% |
| ISO 179 | Impact Strength | 4.86KJ/square meter | 4.66KJ/square meter ,decrease 4.1% |
| Test Method | Characters | Result |
| ASTM D638 | Tensile test | 18.0Mpa |
| ASTM E831 | Coefficient of linear thermal expansion | 40.5 μ m/mC |
| ASTM D256 | Impact resistance | 33.7J/m Type of break: Complete Break |
| ASTM D6109 | Flexural strength |
MOR:29.3Mpa
MOE:3715Mpa |
| ASTM D790 | Flexural properties |
MOR:34.1Mpa
MOE:2503Mpa |
| ASTM D4060 | Abrasion resistance | Weight loss: 0.07g |
| ASTM D6007 | Formaldehyde test | ND ² |
| Country | Sales Quantity in 2023 |
| France | 1000sqm |
| Germany | 10000sqm |
| America | 9000sqm |
| Brazil | 7000sqm |
| Canada | 6500sqm |
| Bulgaria | 5500sqm |
| Romania | 9800sqm |
| Thailand | 4900sqm |
| India | 8600sqm |
| Established | 2004 |
| Factory area: | 36,000 sqm |
| Workshop Area: | 30,000 sqm |
| Annual Turnover: | Average more than USD 10,000,000 |
| Production capacity : | 140 containers/Month |
| Mixed granulating lines: | 7 Domestic lines and 2 Germany lines |
| Extruding lines: | 42 Domestic lines and 5 Austria lines |
| Dealing face lines: | 8 Domestic lines and 1 Germany line |
| Wood grain lines: | 3Domestic Lines |
| Operator: | 128 |
| QC/Engineer: | 10/5 |
| International big projects: | 2008,2012,2016 Olympic Games |