Flux Cored MIG Wire E71t-1c 1.0mm

Model NO.
AWS E71T-1C
Application
Welding Galvanized Sheet, Lap Welding
Welding Position
All Positions
Sample
Available
Aws A5.20 E71t-1c
Aws A5.20 E71t-1c
Transport Package
10kg/Roll, 15kg/Roll, 20kg/Roll
Specification
approved by: ABS, LR, BV, GL, DNV, KR, CCS
Trademark
TOKO
Origin
China
HS Code
83111200
Production Capacity
800 Tons Per Month
Reference Price
$ 1,035.00 - 1,080.00
Contact Us

Product Description

Flux Cored MIG Wire E71t-1c 1.0mm
TOKO AWS A5.20 E71T-1 is formulated to deposit x-ray quality welds in flat, vertical up, horizontal, or overhead positions. E71T-1 is designed for welding low carbon and mild steel, structural and pressure vessel grades. E71T-1 flux core ingredients produce a fast freezing slag that facilitates out of position welds. Bead contour is flat to slightly convex. Slag is easy to remove and low spatter provides easy post weld cleaning.

Instruction

1. Gas- Shielded:Above 99.98% CO2

2. When welding, the gas flow rate shoule keep between 20L/min and 25L/min

3.The oil stains and rust on the welding should be cleared away.

Chemical Composition of Deposited Metal

  C Mn Si P S
Case 0.052 1.4 0.42 0.019 0.011
(W/ CO2)
Standard ≤0.18 ≤1.75 ≤0.90 ≤0.03 ≤0.03
( AWS E71T-1)

Machanical Properties of Deposited Metal

  YP Rel/ Mpa Tensile Strength/ Mpa Elongation % Impact Value
Case 505 570 28 -20°C/ 120
(W/ CO2)
Standard ≥375 490-660 22 27
( AWS E71T-1)

Reference Welding Parameter (DC+)

Specification 1.2 1.4 1.6
( Diameter Size mm)
Volt 23-30 24-36 25-40
Amp 150-300 170-360 200-400
mm 15-25 15-25 20-30
L/min 20-25 20-25 20-25
 

Application

Shipbuilding, Offshore, bridge, pressure vessal and general fabrications etc.

Flux Cored MIG Wire E71t-1c 1.0mm
Diameter: 0.8mm / 0.9mm/ 1.0mm / 1.2mm / 1.6mm / 2.0mm / 2.4mm
Shipping approval: ABS, LR, BV, GL, DNV, KR, CCS 

Flux Cored MIG Wire E71t-1c 1.0mm
Flux Cored MIG Wire E71t-1c 1.0mm
Welding Slags are 100% removed Automatically......TOKO brand Flux Cored Welding Wire E71T-1 1.2MM 


 

 