| Test Parameter | Unit | Result |
| As Supplied Tested at 23ºC and 50% RH | ||
| Specific Gravity | g/ml | 1.3 7 ±0.02 |
| Flow (sag or slump) | mm | 0 |
|
Extrusion Rate
Skin Time |
ml/minute
minute |
135
≤60 |
| Tack-free Time | hour | ≤5 |
| Curing time (5mm) | hour | ≤12 |
| As Cured-after 21 days at 23ºC and 50% RH | ||
| Durometer Hardness, Shore A | Points | 44 |
| Movement Capability | % | ±25 |
| Tensile/Modulus at 50% Elongation | Mpa | 0.59 |
| Tensile/Modulus at 100% Elongation | Mpa | 0.84 |
|
Ultimate Tensile Strength
Ultimate Elongation at Break |
Mpa
% |
1.02
355 |