PU Resin for Make Footwears

Model NO.
HD-4160/HD-2000
Specification
HD-4160/HD-2000
Trademark
HuiDe
Origin
China
HS Code
39095000
Production Capacity
150000 Tons/Year
Reference Price
$ 1.80 - 16.20
Contact Us

Product Description

 
HD-4160 / HD- 2000
:,
Characteristics : low density &mid-hardness
:
Application : sandals and slippers shoe sole
Typical properties of PU resin

Sample
Appearance 		Density
(g/cm 3 @25 o C) 		Viscosity
(mPa·s@40 o C) 		Package Size
(kg/drum)
HD-4160
Clear viscous liquid or waxy solid 		1.13~1.18 1900~2400 220
HD-2000
Colorless or pale yellow liquid 		1.18~1.20 400~700 235
* HD-4160/Cat./H 2 O/Hardener =220kg/3.2 kg/800g/0 kg

Product Performance
Items Unit Value Test Standard
Density g/cm 3 0.32-0.45 GB/T 4472-2011 / DIN 53479
Hardness Shore A 35-55 HG/T 2489-2007 / DIN 53505
Tensile Strength MPa >4 GB/T 10654-2001 / DIN 53504
Elongation % >350 GB/T 10654-2001 / DIN 53504
Angle tear strength kN/m >20 GB/T 529-2008 / DIN ISO 34-1
Flexing cycle 100000 HG/T 2411-2006 / DIN 53578
Abrasion mm 3 <200 GB/T 9867-2008 / DIN 53516

Reactivity
Test Items Unit Value
Ratio of (P+C) and I component - 100/102~105
Material temperature o C A:40~45 / B:38~42
Cream time s 8~10
End of rise time s 45~55
Pinch time s 100~120
Free rise density / g/cm 3 0.21~0.25
Metal mold temperature o C 45~55
Demould time min 3~4
  • ,.
The ratio based on the best value varies with the type and quantity of added paint additives.
  • (,).
The free rise foam density varies with the seasonal variation (temperature, humidity)
  • ,.,.
       
         
         
*POLYOL: HD-4060/Cat./H 2 O/Hardener =220kg/3.2 kg/600g/2 kg

Product Performance
Items Unit Value Test Standard
Density g/cm 3 0.38-0.45 GB/T 4472-2011 / DIN 53479
Hardness Shore A 40-50 HG/T 2489-2007 / DIN 53505
Tensile Strength MPa >4 GB/T 10654-2001 / DIN 53504
Elongation % >350 GB/T 10654-2001 / DIN 53504
Angle tear strength kN/m >20 GB/T 529-2008 / DIN ISO 34-1
Flexing cycle 100000 HG/T 2411-2006 / DIN 53578
Abrasion mm 3 <200 GB/T 9867-2008 / DIN 53516

Reactivity
Test Items Unit Value
Ratio of (P+C) and I component - 100/88~90
Material temperature o C A:40~45 / B:38~42
Cream time s 8~10
End of rise time s 45~55
Pinch time s 100~120
Free rise density / g/cm 3 0.25~0.28
Metal mold temperature o C 45~55
Demould time min 3~4

  • ,.
The ratio based on the best value varies with the type and quantity of added paint additives.
  • (,).
The free rise foam density varies with the seasonal variation (temperature, humidity) PU Resin for Make Footwears
PU Resin for Make Footwears
PU Resin for Make Footwears

PU Resin for Make Footwears

 
.

 